Due to the different polymerization methods of ptfe, there are suspension materials (suspension polymerization) and dispersion materials (dispersion polymerization), namely suspension ptfe, disperse ptfe, the processing methods of the two materials are also different.
Due to the different polymerization methods of ptfe, there are suspension materials (suspension polymerization) and dispersion materials (dispersion polymerization), namely suspension ptfe, disperse ptfe, the processing methods of the two materials are also different.
Suspended material (suspended polytetrafluoroethylene)
Its main forming method is die pressing method, that is, white powder without a little additive, then die pressing forming, sintering above its melting point temperature, and then through appropriate mechanical processing into products, the representative products for the plate, bar, tube, film four categories.
Dispersion material (ptfe)
PTFE fine powder prepared by dispersion polymerization method is generally referred to as “dispersion”.Because of the fibrotic properties of this fine powder, especially at temperatures above 20℃, it is recommended to store, transport and mix the material at 5 ~ 10℃.The forming method of this kind of material is to use an auxiliary agent (usually petroleum ether or gasoline) and powder after mixing in the environment of 24℃ or more for about 24h (complete the crystal phase change) and then forming, with the piston extrusion forming, drying, burning.This processing method is commonly known as paste extrusion, also known as push.
Due to the dispersion of fine powder particle size, divided into several grades of specifications, different specifications have different compression ratio characteristics.Compression ratio of less than 100, generally used to produce raw material and microporous tape;Low compression ratio of less than 500, used to produce medium and large specification products;500 ~ 2000 is medium compression ratio.2000 ~ 4400 is high compression ratio material, this material is suitable for the production of thin wall thin line, can continuously large length and high efficiency production.
Identification method: the main difference is the particle size of the two are not the same.Suspension material is coarse, dispersion material is fine.